| PROPERTY |
TEST Method |
EN ISO 11612規範 |
| 6.2.1 Heat resistance (at 180°C) |
ISO 17493: 2000 at 180°C |
Shall not ignite or melt or shrink ≤ 5% |
| 6.2.2 Heat resistance (at 260°C) |
ISO 17493: 2000 at 260°C |
Shall not ignite or melt or shrink ≤ 10% |
| 6.3.2 Limited flame spread – Face ignition (A1) (tested "as received") |
ISO 15025: 2000 Procedure A |
No flaming to edge
No holing
No melting or flaming
or molten debris
Mean afterflame ≤ 2s
Mean afterglow ≤ 2s
|
| 6.3.2 Limited flame spread – Face ignition (A1) (tested after pre- treatment) |
ISO 15025: 2000 Procedure A |
No flaming to edge
No holing
No melting or flaming
or molten debris
Mean afterflame ≤ 2s
Mean afterglow ≤ 2s
|
| 6.4 Dimensional change |
ISO 5077:2007 |
Knitted: ≤ 5% |
| 6.5.3 Burst strength |
ISO 13938-1:1999 (test area 7.3cm2) |
≧200kPa |
| 6.9.2 pH value |
ISO 3071:2005 |
Greater than 3.5 and less than 9.5 |
| 7.2 Convective heat (Code letter B) |
ISO 9151:1995 |
Grade
HTI24
B1 ≧4.0s
B2 ≧10.0s
B3 ≧20.0s
(based on lowest result) |
| 7.3 Radiant heat (Code letter C) |
ISO 6942:2002 MethodB at 20kW/m2TEST |
Grade RHTI24
C1 ≧7.0s
C2 ≧20.0s
C3 ≧50.0s
C4 ≧95.0s
(based on lowest result) |
| 7.6 Contact heat (Code letter F) |
ISO 12127: 1996 Tc=250℃ |
Grade tt
F1 ≧5.0s
F2 ≧10.0s
F3 ≧15.0s
(based on lowest result) |
No.9-22, Tongwen Ln., Yuchi Township, Nantou County 555, Taiwan (R.O.C.)
+886-49-2899101
service@oxinforce.com.tw
Contact
Send your specification
mark can then be affixed to the approved equipment.